Modello | Composizione | Intervallo di Fusione (°C) | Peso Spec. (g/cm3) | Standard ISO |
---|---|---|---|---|
PRO/L | Cu 60%, Zn 38.49%, Si 0.28%, Mn 0.94%, Sn 0.29% | 870-890 | 8,4 | B Cu 60 Zn Si 870-890 |
PRO/L SUPER | Cu 58%, Zn 41%, Ag 1% (Tracce di Si,Mn e Sn) | 850-870 | 8,5 | B Cu 59 Zn Ag Si 850-870 |
NG 72 F | Cu 49.9%,Zn 41%, Ni 9% (Tracce di Si) | 890-920 | 8,7 | B Cu 49 Zn Ni Si 890-920 |
NG 72 F SUPER | Cu 49%, Zn 41%, Ni 9%, Ag 1% Tracce di Si,Mn e Sn) | 870-900 | 8,7 | B Cu 49 Zn Ni Ag Si 870-900 |
NG 85 | Cu 49%, Zn 41%, Ni 9%, (Tracce di Si) | 890-920 | 8,7 | B Cu 48 Zn Ni (Si) 890-920 |
Modello | Composizione | Intervallo di Fusione (°C) | Peso Spec. (g/cm3) | Standard ISO |
---|---|---|---|---|
AG 2% ARG | Cu 91.3%, P 6.7%, Ag 2% | 650-820 | 8,1 | B Cu 91 P Ag 650-820 |
AG 5% ARG | Cu 89%, P 6%, Ag 5% | 650-810 | 8,2 | B Cu 89 P Ag 650-810 |
AG 10% ARG | Cu 83.8%, P 6.2%, Ag 10% | 650-750 | 8,3 | B Cu 84 P Ag 650-750 |
AG 15% ARG | Cu 80%, P 5%, Ag 15% | 650-800 | 8,4 | B Cu 80 P Ag 650-800 |
AG 65 F | Cu 93.6%, P 6.4% | 710-840 | 8,1 | B Cu 94 P 710-840 |
AG 70 F | Cu 92.8%, P 7.3% | 710-790 | 8,0 | B Cu 93 P 710-790 |
AG 75 F | Cu 92.5%, P 7.5% | 710-770 | 8,0 | B Cu 93 P 710-770 |
AG 80 F | Cu 92%, P 8% | 710-739 | 8,0 | B Cu 92 P 710-739 |
AG 80 | Cu 86%, P 6.75% | 650-700 | 8,0 | B Cu 86 Sn P 650-700 |
Modello | Composizione | Intervallo di Fusione (°C) |
---|---|---|
STAGNO 40% | Sn 40%, Pb 60% | 183-245 |
STAGNO 50% | Sn 50%, Pb 50% | 183-213 |
STAGNO 60% | Sn 60%, Pb 40% | 183-189 |
STAGNO 63% | Sn 63%, Pb 37% | 183 |
Modello | Composizione | Intervallo di Fusione (°C) |
---|---|---|
STAGNO 35% | Sn 35%, Pb 65% | 183-245 |
STAGNO 40% | Sn 40%, Pb 60% | 183-238 |
STAGNO 50% | Sn 50%, Pb 50% | 183-213 |
STAGNO 60% | Sn 60%, Pb 40% | 183-189 |
Modello | Composizione | Intervallo di Fusione (°C) | Peso Spec. (g/cm3) | Standard DIN 8513 |
---|---|---|---|---|
ARG. 5% | Ag 5%, Cu 55%, Zn 40% | 830-870 | 8,2 | LAg 5 |
ARG. 12% | Ag 12%, Cu 48%, Zn 40% | 800-830 | 8,3 | LAg 12 |
ARG. 20% | Ag 20%, Cu 44%, Zn 35.9%, Si | 690-810 | 8,4 | LAg 20 |